Nano silver paste for low temperature sintering
SHAREX'S Nano silver paste AS 9120 can be sintered at 120℃low temperatures. As pastes, they can be made into printed circuits at low temperatures. They are particularly suitable for printing on organic substrates, including PET film, which cannot be subjected to high temperatures.
SHAREX AS 9120 Features:
Composed of silver paste of 120-200 nm average diameter, organic polymers and organic solvents.
By curing (100℃~250℃) under air, low resistance sintered Ag layer can be forme .
Wires of less than 70 µm can be printed by screen-printing.
Printed wires are highly durable when bent.
After a printed wire had been bent 100,000 times (bending radius R= 0.5mm), no change in resistance was observed.